The hanit® material consists of recycled plastics, to be more precise, polyolefin mixtures. The main components of these blends are polyethylene (LDPE/HDPE) and polypropylene (PP).
Through utilization of these high-quality recycled raw-materials (material purity level > 95 %) expensive new material is replaced and environmental resources are conserved.
Our customers are repeatedly impressed by the functionality, simple handling, robustness and durability of this material.
Verifiable practical experience from various fields of application and under the toughest conditions have shown that hanit® is an innovative material.
- Electrically non-conductive
- Fire behaviour: Fire Class B2 (DIN 4102)
- Pressure resistant
- Density: approx. 0.93 g/cm³
- Low thermal conductivity, the thermal conductivity value is about 0.23 [W/mK]
- Continuous operating temperature: - 20 to + 50 °C
- Waterproof (hydrophobic)
- Resistant to oils, alkalis, acids and seawater
- Resistant to micro-organisms
- High splinter resistant
- Fully pigmented
|hanit® Quality 1||hanit® Quality 3|
|Testing:||Standard DIN EN ISO||Unit||Measured value||Standard
|Tensile modulus of elasticity||527-1||MPa||405.20||94.60||742.20||61.50|
|Nominal elongation at rupture||527-2||%||151.40||78.30||11.09||2.51|
|Tensile stressed at yield||527-2||MPa||15.25||0.44||12.64||1.44|
|Elongation at yield||527-2||%||21.39||0.84||9.18||1.96|
|Elongation at tensile strength||527-2||%||138.20||85.90||9.18||1.96|
|Flexural modulus of elasticity||178||MPa||269.20||84.40||641.80||50.40|
|Flexural stress at 3.5 % outer fibre strain||178||MPa||10.09||1.48||18.42||0.69|
|Flexural stress at Fmax.||178||MPa||13.66||1.76||21.87||0.82|
Our raw material hanit® as well as the products made from it are constantly tested and certified in regard to multiple aspects. PDF files of corresponding test reports, results, certificates and attestations are available in our Download Centre.